PH vlekvrye staal

Jy is hier : home>Produk>materiaal>PH vlekvrye staal

  • https://www.alloy-ronsco.com/upload/product/1634525013225227.jpg
  • https://www.alloy-ronsco.com/upload/product/1634525025131045.jpg
  • https://www.alloy-ronsco.com/upload/product/1634525025892323.jpg
  • https://www.alloy-ronsco.com/upload/product/1634525025243791.jpg
  • https://www.alloy-ronsco.com/upload/product/1634525025910296.jpg
  • https://www.alloy-ronsco.com/upload/product/1634525026968793.jpg
  • 1
  • 2
  • 3
  • 4
  • 5
  • 6

China vervaardiger spesiale staal Hoë kwaliteit vlekvrye staal 15-5PH Bar

Standaard: JIS, AISI, ASTM, GB, DIN, EN
Lengte: 1000 ~ 6000 mm, of pasgemaak.
MOQ: 0.5 Ton

  • Produk Beskrywing
  • ondersoek

Model: 15-5PH / S15500 / XM-12 / W.Nr.1.4545
Handelsmerk: RONSCO
Kode: Alloy1996H15-5PH


Inleiding:

15-5PH is a martensitic precipitation-hardening stainless steel that provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600F (316C) and good toughness in both the longitudinal and transverse directions in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling.
15-5PH is the ferrite-free version of 17-4PH Stainless Steel. Both alloys are widely used in theaerospace, chemical, petrochemical, food processing, paper and general metalworking industries.
Soortgelyke grade:DIN 1.4545, UNS S15500, 15-5PH

Vorm:Round, Flat, Square.

Grootte reeks:


Diameter (mm)Dikte (mm)Breedte (mm)Lengte (mm)
Round20-480--2000-5800
Square20-480--2000-5800
plat-20-5080-6002000-5800

Steel-making Condition:

EF, EF/EAF+LF+VD, EF/EAF+ESR

Afleweringstoestand:

Annealed , Quenched + Tempered

Oppervlakte toestand:

Black, Grinded, Peeled, Rough turned, Polished

Chemiese samestelling:

CMnPSSiCrNiCuNB + Ta
0.07max1.0max0.030max0.035max1.0max14.0-15.03.5-5.52.5-4.50.15-0.45

Meganiese eienskappe

Delivey ConditionModuls of Elasticity(GPa)Moduls of Rigidity(GPa)Treksterkte Rm (Mpa)Yield Strength Rp0.2 (Mpa)Elongation % in 2″ (50.8 mm)Reduction Of Area (%)Hardheid (HRC)
A(annealed)//////35 maksimum
H 900197.677.31378 min1276 min14 min50min44min
H925//1309 min1207 min14 min54min42min
H1025/75.91173 min1138 min15 min56min38min
H1075/691138 min1035 min16 min58min36min
H1100//1035 min931 min17 min58min34min
H1150/691000 min862 min19 min60min33min