China vervaardiger spesiale staal Hoë kwaliteit nikkel-gebaseerde legering Hastelloy X

HastelloyX is a nickel-chromium-molybdenum alloy with cobalt and tungsten added. HastelloyX alloy has excellent oxidation resistance at high temperatures up to 1200°C and can also be used in neutral and reducing atmospheres. At the same time, HastelloyX alloy can resist carbonization and nitriding atmosphere.

  • Produk Beskrywing
  • ondersoek

Model: HastelloyX
Handelsmerk: Ronsco
Kode: 7507120000


HASTELLOY X

ASTM B435, B366, B572, B619 B622, B626, B751, B775, B829
UNS-nommer N06002
DIN 2.4665

Other common names: Alloy X, Inconel HX
Hastelloy X is a nickel-chromium-iron-molybdenum superalloy with outstanding high temperature strength, oxidation resistance, and fabricability. Alloy X’s oxidation resistance is excellent up to 2200° F. This nickel steel alloy has also been found to be exceptionally resistant to stress-corrosion cracking in petrochemical applications. Matrix stiffening provided by the molybdenum content results in high strength in a solid-solution alloy having good fabrication characteristics. Although this nickel alloy is primarily noted for heat and oxidation resistance it also has good resistance to chloride stress-corrosion cracking, carburization, and excellent resistance to reducing or carburizing atmospheres. Two common conditions that often lead to early failure in high temperature alloys, carburization and nitriding, Hastelloy X resists.


In what forms is Hastelloy X ?

Sheet
Plate
bar

What are the characteristics of Hastelloy X?
Outstanding oxidation resistance through 2000°F
Resistant to carburization and nitriding
Uitstekende hoë temperatuursterkte
Good resistance to chloride stress-corrosion cracking

Chemiese samestelling(%)
Ni Mo Cr Fe W Co Mn C
Restant 8.0-10.0 20.5-23.0 17.0-20.0 .2-1.0 .5-2.5 1.0 maksimum .05-.15
P S Si Al Ti B Cu
.04 maks .03 maks 1.0 maksimum .50 maks .15 maks .01 maks .50 maks

In what applications is Hastelloy X used?

Gas turbines

Petrochemiese bedryf

Industriële oonde

Heat treating equipment

Kerningenieurswese

Jet engine combustion chambers

Aircraft cabin heaters

Turbine exhaust components


Alloy X is one of the most widely used nickel base superalloys for gas turbine engine combustion zone components such as transition ducts, combustor cans, spray bars and flame holders as well as in afterburners, tailpipes and cabin heaters. It is recommended for use in industrial furnace applications because it has unusual resistance to oxidizing, reducing and neutral atmospheres. Hastelloy X is also used in the chemical process industry for retorts, muffles, catalysts support grids, furnace baffles, tubing for pyrolysis operations and flash drier components.


Fabrication with Hastelloy X

Alloy X has excellent forming and welding characteristics. It can be forged and, because of its good ductility, can be cold worked. It can be welded by both manual and automatic methods including shielded metal arc, gas tungsten arc, gas metal arc and submerged arc processes. The alloy can also be resistance welded. For hot forming, the alloy should be heated to a starting temperature of 2150° F (1175°C).


ASTM spesifikasies

Vel / Plaat bar
B435 B572

Meganiese eienskappe

Representative Tensile Properties, sheet

Temp° F Tensile (psi) .2% Yield (psi) Elongation in

2 "%

70 110,600 54,900 44
1000 89,000 35,600 49
1200 83,000 35,400 54
1400 67,000 34,400 53
1600 45,000 28,200 58

 